Effect of The Cold Working on Mechanical Properties of Aluminum Produced From Waste Beverage Cans


GÜRBÜZ M.

Dokuz Eylül Üniversitesi Mühendislik Fakültesi Fen ve Mühendislik Dergisi, vol.20, no.58, pp.28-35, 2018 (Peer-Reviewed Journal) identifier

Abstract

In this study, aluminum based waste beverage cans were recovered by casting method. Cold working at different percentage were applied to improve mechanical properties of casted aluminum. The mechanical properties of aluminum materials before and after cold working were performed with hardness and tensile strength measurement. Microstructure and crystal structure of materials were analyzed with scanning electron microscopy and X-ray diffraction devices. From the results the mechanical properties were improved up to %31 cold working rate. The Vickers hardness increased from 76HV to 102HV. Tensile strength increased from 54MPa to 92MPa with increasing cold working rate
Bu çalışmada, döküm yöntemi ile alüminyum esaslı atık içecek kutularının geri kazanımı sağlanmıştır. Dökümü yapılan alüminyumun mekanik özelliklerini iyileştirmek için farklı yüzde oranlarında soğuk işlem uygulanmıştır. Soğuk işlem öncesi ve sonrası alüminyum malzemelerin mekanik özellikleri sertlik ve çekme dayanımı ölçümü ile belirlenmiştir. Malzemelerin mikroyapısı ve kristal yapısı taramalı elektron mikroskobu ve Xışını kırınımı cihazı ile analiz edilmiştir. Elde edilen sonuçlardan soğuk şekil değişimi miktarı %31'e kadar arttıkça mekanik özelliklerin iyileştiği görülmüştür. Artan soğuk şekil değişimine bağlı olarak Vikers sertlik değeri 76HV'den 102HV'ye, çekme dayanımı ise 54MPa'dan 92 MPa'ya kadar artmıştır