Aluminum-based composites are frequently utilized in various industrial areas (aviation, automotive, space industry, etc.) because they have lightweight structure, good thermal and electrical conductivity, and high mechanical strength. In this study, carbon nanotube (CNT) reinforced (0.1-0.5% by weight) Al6061 alloy matrix composites were fabricated via hot-pressing and powder metallurgy methods. The phase structure and microstructure of the produced specimens were analyzed, and their experimental density, porosity ratio, hardness, and compressive strength were determined. As a result of the performed tests, it was seen that hardness and compressive strength of the Al6061-0.1%CNT composite improved by 10.2% and 21%, respectively, compared with Al6061 alloy. Consequently, it is determined that carbon nanotube contribution up to a certain percentage (0.1wt.%) improves mechanical properties, and carbon nanotube is an effective reinforcement element for aluminum matrix composites.
Alüminyum esaslı kompozitler; hafif olmaları, iyi ısıl ve elektriksel iletkenliğe sahip olmaları, mekanik dayanımlarının yüksek olması sebebiyle çeşitli endüstriyel alanlarda (havacılık, otomotiv, uzay sanayi vb.) sıklıkla kullanılmaktadır. Bu çalışmada, toz metalürjisi ve sıcak presleme yöntemleriyle karbon nanotüp (KNT) katkılı (ağırlıkça %0,1-0,5) Al6061 esaslı kompozitler üretilmiştir. Üretilen numunelerin faz yapısı ve mikroyapısı analiz edilip deneysel yoğunluğu, gözeneklilik oranı, sertliği ve basma dayanımı tespit edilmiştir. Yürütülen testler sonucunda Al6061 alaşımına kıyasla Al6061-%0,1KNT kompozitin sertliğinin ve basma dayanımının sırasıyla %10,2 ve %21 oranlarında iyileştiği görülmüştür. Sonuç olarak karbon nanotüp katkısının ağırlıkça belirli bir orana (%0,1) kadar mekanik özellikleri iyileştirdiği ve karbon nanotüpün alüminyum matrisli kompozitler için etkili bir takviye elemanı olduğu belirlenmiştir.